1. 毕业设计（论文）的内容和要求

ti-al基金属间化合物密度仅为3.8~4.0g/cm3，是镍基高温合金的1/2，比钛合金还低10%；室温弹性模量高达160~170gpa，比钛合金高30%，而且弹性模量在750℃高温还能保持150gpa，与gh4169高温合金相当。

ti-al基合金还具有高比强度，室温800℃时强度保持率达到80%，具有高蠕变抗力，优异的抗氧化和阻燃性能，可在760℃~800℃长期工作。

基于ti-al基合金的综合性能优势，在航空航天高温应用条件下可以用来代替其他高温合金从而获得明显的减重效果。

2. 参考文献

[1]章德铭, 陈贵清, 韩杰才, 孟松鹤. γ-TiAl基高温结构材料研究评述. 中国稀土学报 2005:163-7. [2]张秋平. γ-TiAl金属间化合物的研发进展. 飞航导弹 2007:59-62. [3] 陈玉勇, 张树志, 孔凡涛, 刘祖岩, 林均品. 新型β-γTiAl合金的研究进展. 稀有金属 2012:154-60. [4]APPEL F, OEHRING M, PAUL J D H. Nano-scale design of TiAl alloys based on β-phase decomposition [J]. Advanced Engineering Materials, 2006, 8: 371#8722;376. [5]ZHANG B, WANG J N, YANG J. Superplastic behavior of a TiAl alloy in its as-cast state original research article [J]. Materials Research Bulletin, 2002, 37: 2315#8722;2320. [6]CLEMENS H, WALLGRAM W, KREMMER S, G THER V, OTTO A, BARTELS A. Design of novel β-solidifying TiAl alloys with adjustable β/B2-phase fraction and excellent hot-workability [J]. Advanced Engineering Materials, 2008, 10: 707#8722;713. [7] 李臻熙.TiAl 合金组织控制对力学性能的影响[D]. 北京航空材料研究院. [8] 许正芳, 徐向俊, 林均品等. 热处理对大尺寸铸态高 Nb-TiAl 合金组织中S-偏析的影响[J]. 航空材料学报, 2007, (03):113-117. [9]陈玉勇，孔凡涛. TiAl 合金显微组织细化. 金属学报，2008，5：551-556. [10]张鹏.粉末冶金制备 Ti-45Al-5Nb 合金工艺及其组织性能研究：[硕士学位论文]. 哈尔滨：哈尔滨工业大学，2013. [11]Y. W. Kim. Ordered intermetallic alloys (III)--gamma titanium aluminides. JOM. 1994(46):30-39. [12] E. Schwaighofer, H. Clemens, S. Mayer, J. Lindemann, J. Klose, W.Smarsly, and V. Gu#168;ther, Microstructural Design and Mechanical Properties of a Cast and Heat Treated Intermetallic Multi-phase γ -TiAl Based Alloy, Intermetallics, 2014, 44, p 128#8211;14039(23):34-37. [13]J. Yang, J.N. Wang, Q. Xia, and Y. Wang, Effect of Cooling Rate on the Grain Refinement of TiAl-Based Alloys by Rapid Heat Treatment, Mater. Lett., 2000, 46, p 193#8211;197. [14]A. Koscieln and W. Szkliniarz, Effect of Cyclic Heat Treatment Parameters on the Grain Refinement of Ti-48Al-2Cr-2Nb Alloy, Mater. Charact., 2009, 60, p 1158#8211;1162. [15] J.N. Wang, J. Yang, and Y. Wang, Grain Refinement of a Ti-47Al-8Nb-2Cr Alloy Through Heat Treatments, Scr. Mater., 2005, 52, p329#8211;334. [16] Su MK, Zheng LJ, Lang ZB, Yan J, Zhang H. Microstructural evolution of a PM TiAl alloy during heat treatment in alpha plus gamma phase field. Rare Met. 2012;31(5):424. [17] Han J C , Xiao S L , Tian J , et al. Microstructure characterization and tensile properties of a Ni-containing TiAl-based alloy with heat treatment[J]. Rare Metals, 2016, 35(1):26-34.

3. 毕业设计（论文）进程安排

2018.12.25~2019.1.10 查阅中外文资料，翻译外文资料，参加讨论。

2019.1.10~2019.1.20 撰写开题报告，参加开题答辩。

2019.3.1~2019.3.8 制定研究方案，熟悉仪器，参加讨论。