论文总字数：17609字

摘 要

聚丁二酸丁二醇酯（PBS）因其本身优异的力学性能、易机械加工、良好的耐热性和耐化学腐蚀，在近年来受到国内外材料领域的高度重视，因而成为了可降解聚酯中发展较快的品种之一，前景不可限量。本文以聚丁二酸丁二醇酯（PBS）为主要原料，按一定的配比加入小麦蛋白(WP)通过密炼机进行熔融共混，放入手动压片机中进行压片，制样后通过万能试验机进行拉伸性能测试和电子分析天平测试吸水率。

通过试验结果表明：加入小麦蛋白后，复合材料的拉伸强度和断裂伸长率都呈下降趋势，且随着小麦蛋白的增加而降低。当小麦蛋白的添加量为20 %时，拉伸强度较纯料降低了35.6 %，为23.38 MPa。当小麦蛋白添加量为40 %时，拉伸强度下降最明显，拉伸强度较纯料降低了 57.6 %，拉伸强度为15.38 MPa。吸水率测试表明：当小麦蛋白的添加量为20%时，吸水率是0.33%，较纯料降低了53.5 %。当小麦蛋白添加量为40 %时，吸水率为0.83 %，较纯料提高了16.9 %，呈先下降后上升的趋势。

关键词：聚丁二酸丁二醇酯 ；小麦蛋白；拉伸强度；吸水率

Structure and properties of PBS / wheat protein composite

ABSTRACT

In recent years, due to its excellent mechanical properties, easy machining, good heat resistance and chemical corrosion resistance, PBS has attracted great attention in the field of materials at home and abroad, so it has become one of the fast developing varieties of degradable polyester, and its prospect is unlimited. In this paper, poly PBS was used as the main raw material, and wheat protein (WP) was added in a certain proportion to melt and blend through a mixer, and then put into a manual tablet press for tablet pressing. After sample preparation, the tensile properties were tested by a universal testing machine and the water absorption was tested by an electronic analytical balance.

The results showed that the tensile strength and elongation at break of the composite decreased with the addition of wheat protein. And it decreased with the increase of wheat protein. When the content of wheat protein was 20 %, the tensile strength decreased by 35.6 % and 23.38 MPa When the content of wheat protein was 40%, the tensile strength decreased most obviously. The tensile strength decreased 57.6 % and 15.38 MPa. The test of water absorption showed that when the content of wheat protein was 20%, the water absorption was 0.33 %, which was 53.5 % lower than that of the pure material. When the content of wheat protein was 40%, the water absorption was 0.83 %, which was 16.9 % higher than that of the pure material.

Key Words: PBS; Wheat protein; Tensile strength; Water absorption

目 录

摘要 I

ABSTRACT II

第一章绪论 1

1.1聚丁二酸丁二醇酯概述 1

1.1.1PBS简介 1

1.1.2PBS的合成和制备 1

1.1.3 PBS的基本性质 3

1.1.4 PBS的应用领域 4

1.2 PBS的改性研究 5

1.2.1共混改性 5

1.2.2共聚改性 5

1.2.3扩链改性 6

1.3PBS共混改性意义及进展 6

1.3.1PBS完全生物降解高分子混合体系 6

1.3.2无机填料共混高分子体系 7

1.3.3高分子合金共混体系 7

1.4小麦蛋白概述 8

1.4.1小麦蛋白的简述 8

1.4.2小麦蛋白的改性 8

1.4.3小麦蛋白的应用领域 9

1.5课题背景 10

1.6研究内容和方法 11

1.6.1研究内容 11

1.6.2研究方法 11

第二章实验部分 12

2.1主要原料 12

2.2主要设备 12

2.3试样制备 12

2.3.1 PBS/小麦蛋白复合材料的制备 12

2.3.2样条的制备 13

2.4测试与表征 13

2.4.1力学性能测试 13

2.4.2吸水性能测试 13

第三章 结果与讨论 14

3.1力学性能 14

3.1.1拉伸强度 14

3.1.2断裂伸长率 16

3.2吸水性能 16

第四章结论与展望 18

4.1结论 18

4.2展望与不足 18

参考文献 20

致谢 23

第一章 绪论

1.1 聚丁二酸丁二醇酯概述

1.1.1 PBS简介

现在资源的不可再生问题和白色污染问题愈发严重，因此我国制订了很多法律法规来全面抑制白色污染问题，但这只能控制和减少塑料袋的使用，并不能从根源上解决白色污染问题，因此是否能开发和使用生物可降解材料变得至关重要。

生物可降解塑料有很多包括：聚丁二酸丁二醇酯（PBS）、聚羟基烷酸酯（PHA）、聚乙烯醇（PVA）等。PBS与其他可降解塑料相比，其在价格成本，力学性能，热稳定性，生物降解性等方面都有着一定的优势，它在生物降解塑料方面将会是一个研究的重点。

请支付后下载全文，论文总字数：17609字