摘 要

在工业生产中，许多机械零件是通过塑性变形制成的，而腐蚀则往往伴随着零件的产生。在零件的表面加防腐涂层必不可少，对机械零件加工时留下的塑性变形与腐蚀程度的具体关系是本论文研究的核心目的。

本论文对钢板试样变形后进行了腐蚀研究，探究了钢板的塑性变形区的腐蚀程度。最终获得的结果表明：无论是钢板的拉深还是弯曲，塑形变形区与未变形区均发生了腐蚀现象；材料塑形变形区的腐蚀比未发生变形区的腐蚀要更加严重；对于拉深试样，拉深系数越小，腐蚀程度越严重；对于弯曲试样，弯曲的角度越小，腐蚀程度越严重。这个结论对零件的防腐工作有着巨大的参考价值，零件表面中出现的较大塑性变形区要着重添加防腐材料，保护变形区，减缓零件的整体腐蚀。

本文有如下的特色：通过电子探针、线切割、拉深、弯曲、中性盐雾试验等诸多实验和众多钢板试样从多方面证明了材料发生塑性变形后会使腐蚀变得更为严重，根据诸多实验数据绘制了拉深系数和失重率的关系图、弯曲角度和失重率的关系图。

关键词：塑性变形；拉深；弯曲；腐蚀

Abstract

In industrial production, many mechanical parts are made by plastic deformation, and the corrosion is often along with it. Using antiriot material on the surface of parts is essential. During mechanical parts processing, the specific relation between degree of plastic deformation and the degree of corrosion is the main purpose of this paper.

In this paper, by utilizing steel plates the writer studied the relationship between the plastic deformation and the corrosion, and studied the corrosion degree of the plastic deformation zone. The research results show that for drawing samples, the smaller the drawing coefficient is, the more serious the corrosion degree is. As for bending samples, the smaller the bend angle is, the more serious the corrosion degree is. Final conclusion based on the combination of the two factors is: plastic deformation area and the area without deformation occurred with corrosion. Moreover, the corrosion degree of plastic deformation area is more serious than the area without deformation. This conclusion has great reference value for the anticorrosion work of the parts. The larger plastic deformation area should pay more attention to the anti-corrosion materials appending, so that it can effectively protect the deformation area to slow down the corrosion rate of whole parts.

There has some characteristics in this paper: by doing a lot of tests, such as electronic probe test, line cutting experiment, deep drawing test, bending test, and neutral salt spray test, the study from many aspects proved materials of the plastic deformation will make the corrosion becomes more serious. In addition, this paper has drawn two charts, one is the drawing coefficient and the rate of weight loss, the other is the chart of bend angle and the rate of weight loss according to a large number of experimental data.

Key Words：Plastic deformation; drawing; bending; corrosion

目 录

第1章 绪论 1

1.1 研究目的及意义 1

1.2 国内外发展现状 1

1.2.1 冲压国内外发展现状 1

1.2.2 盐雾试验概况 2

1.3 实验操作方案 3

1.3.1 研究内容 3

1.3.2 实验目标 3

1.3.3 具体技术方案 3

第2章 电子探针 5

2.1 电子探针概述 5

2.2电子探针结果 5

第3章 线切割 7

3.1 用线切割的原因 7

3.2 线切割3B代码 7

3.3 本章小结 9

第4章 拉深 10

4.1拉深概述 10

4.2拉深方案 10

4.3本章小结 11

第5章 弯曲 12

5.1弯曲概述 12

5.2弯曲方案 12

5.3本章小结 13

第6章 中性盐雾试验 14

6.1准备工作 14

6.2盐雾试验中 15

6.2.1第一周期（2h） 15

6.2.2第二周期（6h） 16

6.2.3第三周期（24h） 17

6.2.4第六周期（96h） 18

6.2.5第九周期（240h） 19

6.3本章小结 21

第7章 数据处理 22

7.1误差分析 22

7.2原始数据与整理 22

7.3数据结果及分析 28

7.3.1拉深系数和失重率的关系 28

7.3.2弯曲角度和失重率的关系 29

7.4本章小结 30

第8章 结论与展望 31

8.1研究结论 31

8.2展望 31

参考文献 32

致 谢 33

第1章 绪论

1.1 研究目的及意义

在日常的生活中，材料的腐蚀无时无刻在发生着。众所周知，腐蚀是双面性的：腐蚀会给人类带来危害，轻则造成经济损失，重则造成人员伤亡；同时，腐蚀也可以为人类造福：现代工业中经常用到腐蚀进行材料的加工，能有效提高工艺技术指标。在这个背景下进而引发的思考：对于给定材料的不同变形程度，它们腐蚀程度的关系会是怎样的呢？塑性变形区与未变形区的腐蚀程度是否相同？

本研究的目的是得出成形变形程度与材料腐蚀性能的具体关系，它涉及两个方面：一方面是材料的冲压成型，另一方面是材料的腐蚀。本次研究就是要将一种选定的金属材料通过拉深和弯曲，得出不同的拉深系数和弯曲角度等参数，再与盐雾试验相结合，进而具体得出材料的变形程度与腐蚀的关系。研究出这两者的关系，就能明确在哪些区域腐蚀程度大，必要时可添加防腐涂层；在工业生产中该如何控制材料的变形程度以减轻成型件或制品腐蚀的程度，对工业和社会的发展有相当大的益处。

1.2 国内外发展现状